Carbon Steel Alloy Steel Low Temp Pipe & Tubes Specification Table
CHEMICAL ANALYSIS Mechanical  Properties SPECIFIC REQUIREMENT
Tensile  Yield  Elongation
                  Strength Strength    
Specification WT C% Mn% P% max S% max Si% Cr% Mo% Mpa Mpa 50mm min   
Longitudinal
ASTM A 53/A AW 0.25max 0.95max 0.05 0.06 - - - 331min 207 min 36 Cr Mo Cu Ni Va
ASTM A 53/B AW 0.30max 1.20max 0.05 0.06 - - - 413min 240min 29.5 0.40 0.15 0.40 0.40 0.08
ASTM A 106/A AW 0.25max 0.27-0.93 0.025 0.025 0.10min 0.40max 0.15max 330min 205min 35/28 five elements not to exceed 
ASTM A 106/B AW 0.30max 0.29-1.06 0.025 0.025 0.10min 0.40max 0.15max 415min 240min 30/22 1%
ASTM A 106/C AW  0.35max  0.29-1.06 0.025 0.025 0.10min 0.40max  0.15max 485min 275min 30/22  
ASTM A 179 MW 0.06-018 0.27-0.63 0.048 0.048 - - - 325min 180min 35 Hardness 72 HRB max
ASTM A 214 MW 0.18max 0.27-0.63 0.05 0.05 - - - 385min 180min 35 Hardness 72 HRB max
ASTM A 192 MW 0.06-0.18 0.27-0.63 0.048 0.048 0.25max - - 325min 180min 35 Hardness 77 HRB max
ASTM A 209/T1 MW 0.10-0.20 0.30-0.80 0.045 0.045 0.10-0.50 - 0.44-0.65 380min 205min 30/22 Hardness 80 HRB max
ASTM A 209/T1a MW 0.15-0.25 0.30-0.80 0.045 0.045 0.10-0.50 - 0.44-0.65 365min 195min 30/22 Hardness 81 HRB max
ASTM A 209/T1B MW 0.14max 0.30-0.80 0.045 0.045 0.10-0.50 - 0.44-0.65 415min 220min 30/22 Hardness 77 HRB max
ASTM A 210/A-1 MW 0.27max 0.93max 0.048 0.058 0.10min - - 415min 255min 30/22 Hardness 79 HRB max
ASTM A 210/C MW  0.35max  0.29-1.06 0.048 0.058 0.10min -  -  485min 275min 30/22 Hardness 89 HRB max 
ASTM A 213/T2 MW 0.10/0.20 0.30-0.61 0.045 0.045 0.10-0.30 0.50-0.81 0.44-0.65 415min 205min 30/22 Hardness 85 HRB max
ASTM A 213/T5 MW 0.15max 0.30-0.60 0.03 0.03 0.50max 4.00-6.00 0.44-0.65 415min 205min 30/22 Hardness 85 HRB max
ASTM A 213/T11 MW 0.15max 0.30-0.60 0.03 0.03 0.50-1.00 1.00-1.50 0.44-0.65 415min 205min 30/22 Hardness 85 HRB max
ASTM A 213/T12 MW 0.15max 0.30-0.61 0.045 0.045 0.50max 0.80-1.25 0.44-0.65 415min 220min 30/22 Hardness 85 HRB max
ASTM A 213/T22  MW 0.15max 0.30-0.60 0.03 0.03 0.50max 1.90-2.60 0.87-1.13 415min 205min 30/22 Hardness 85 HRB max 
ASTM A 333/1 AW 0.30max 0.40-1.06 0.025 0.025 - - - 380min 205min 25/20 Impact AS-50F
ASTM A 333/6 AW 0.30max 0.29-1.06 0.025 0.025 0.10min - - 415min 240min 30/22 FOR 40X10J/18/14
ASTM A 334/1 AW 0.30max 0.40-1.06 0.025 0.025 - - - 380min 205min 35/28 -50F 40X10J/18/14
ASTM A 334/6 AW  0.30max 0.29-1.06 0.025 0.025 0.10min -  -  415min 240min  30/22  90 HRB max
ASTM A 335/P1 AW 0.10-0.20 0.30-0.80 0.025 0.025 0.10-0.50 - 0.44-0.65 380min 205min 30/22  
ASTM A 335/P2 AW 0.10-0.20 0.30-0.61 0.025 0.025 0.10-0.30 0.50-0.81 0.44-0.65 380min 205min 30/22  
ASTM A 335/P5 AW 0.15max 0.30-0.60 0.025 0.025 0.50max 4.00-6.00 0.45-0.65 415min 205min 30/22  
ASTM A 335/P9 AW 0.15max 0.30-0.60 0.025 0.025 0.25-1.00 8.00-10.00  0.09-1.10 415min 172min 30/22  
ASTM A 335/P11 AW 0.15max 0.30-0.60 0.025 0.025 0.50-1.00 1.00-1.50 0.44-0.65 415min 205min 30/22  
ASTM A 335/P12 AW 0.15max 0.30-0.61 0.025 0.025 0.50max 0.80-1.25 0.44-0.65 415min 205min 50/22  
ASTM A 335/P22  AW  0.15max 0.30-0.60 0.025 0.025 0.50max 1.90-2.60 0.87-1.13 415min 205min  30/22   
BS/3059/1/33   0.15max 0.30-0.70 0.05 0.05 - - - 324-441 186min 25  
BS/3059/2/33   0.15max 0.40-0.70 0.05 0.05 0.10-0.35 - - 324-441 186min 21  
BS/3059/2/45   0.12-0.18 0.90-1.20 0.035 0.035 0.10-0.35 - - 441-560 245min 22  
BS/3059/2/620    0.10-0.15 0.40-0.70 0.04 0.04 0.10-0.35 0.70-1.10  0.45-0.65  441-618 235min 22  
DIN/17175/ST35.8   0.17max 0.40min 0.04 0.04 0.35max - - 340-441 235min 25  
DIN/17175/ST45.8   0.22max 0.45min 0.04 0.04 0.10-0.35 - - 441-540 255min 25  
DIN/17175/15MO3   0.12-0.20 0.50-0.80 0.04 0.04 0.10-0.35 - 0.25-0.35 441-540 284min 21  
DIN/17175/13CrMO44   0.10-0.18 0.40-0.70 0.04 0.04 0.10-0.35 0.70-1.60 0.40-0.50 441-570 294min 22  
DIN/17175/10CrM910    0.15max 0.40-0.60 0.04 0.04 0.15-0.50 2.0-2.5  0.9-1.10  441-570 294min 22  
ASTM A 199/T5 MW 0.50-0.15 0.30-0.60 0.03 0.03 0.50max 4.00-6.00 0.45-0.65 415min 170min 30/22 Hardness 85 HRB max
ASTM A 199/T11 MW 0.50-0.15 0.30-0.60 0.03 0.03 0.50-1.00 1.00-1.50 0.44-0.65 415min 170min 30/22 Hardness 85 HRB max
ASTM A 199/T22 MW 0.50-0.15 0.30-0.60 0.03 0.03 0.50max 1.90-2.60 0.87-1.13 415min 170min 30/22 Hardness 85 HRB max
ASTM A 199/T4 MW 0.15max 0.30-0.60 0.03 0.03 0.50-1.00 2.15-2.85 0.44-0.65 415min 170min 30/22 Hardness 85 HRB max
ASTM A 199/T7 MW 0.15max 0.30-0.60 0.03 0.03 0.50-1.00 6.00-8.00 0.45-0.65 415min 170min 30/22 Hardness 85 HRB max
ASTM A 200/T5 MW 0.15max 0.30-0.60 0.03 0.03 0.50-1.00 4.00-6.00 0.45-0.65 415min 170min  30/22 Hardness 85 HRB max
ASTM A 200/T11 MW 0.50-0.15 0.30-0.60 0.03 0.03 0.50-1.00 1.00-1.50 0.44-0.65 415min 170min 30/22 Hardness 85 HRB max
ASTM A 200/T22 MW 0.50-0.15 0.30-0.60 0.03 0.03 0.50max 1.90-2.60 0.87-1.13 415min 170min 30/22 Hardness 85 HRB max
ASTM A 200/T4 MW 0.50-0.15 0.30-0.60 0.03 0.03 0.50-1.00 2.15-2.85 0.44-0.65 415min 170min 30/22 Hardness 85 HRB max
ASTM A 200/T7 MW 0.15max 0.30-0.60 0.03 0.03 0.50-1.00 6.00-8.00 0.45-0.65 415min 170min 30/22 Hardness 85 HRB max
ASTM A 199/T9 MW 0.15max 0.30-0.60 0.03 0.03 0.25-1.00 8.00-10.0 0.90-1.10  415min  170min 30/22  Hardness 85 HRB max